LL20200 FE is a butene linear low-density polyethylene designed for the blown and cast film extrusion
processes, offering balanced combination of physical and mechanical properties. Films produced from this resin
have improved tensile strength, toughness, optical properties and high cling performance.

TYPICAL APPLICATIONS
LL20200 FE is recommended for the production of mono- and multilayer blown films for general purpose
applications, frozen food bags, lamination and coextruded films, carrier and garbage bags, industrial liners, hand
and pallet stretch wrap films. It is suitable for blending with LDPE both in cast and blown film.

Properties	Conditions	Method	Typical values*	Units
Resin properties
Melt Flow Rate	190 °C/2.16 kg	ISO 1133	3	g/10 mi
Density		ISO 1133	0.920	g/cm3
Film properties measured on 20 μm film
Tensile strength at break	MD/TD	ISO 527-1	30/19	MPa
Elongation at break	MD/TD	ISO 527-1	550/750	%
Tensile stress at yield	MD/TD	ISO 527-1	10/8	MPa
Elmendorf Tear Strength	MD/TD	ASTM D1922	100/300	g/25 μm
Dart Drop Impact Strength	MD/TD	ASTM D1709	90	g
1% Secant modulus	MD/TD	ASTM D1184	80/100	MPa
Haze		ASTM D 1003	1	%
Gloss (45 °C)		ASTM D 2457	1	0,00%
Thermal			95
Vicat Softening Temperature	10 N	ISO 306	97	°C

*The values given are typical values measured on the product. These values should not be considered as specification.
**Properties were measured on film extruded at a blow up ratio 2:1 with a melt temperature of 225 °C.